Mixed catalyst composition

ABSTRACT

The present invention relates to catalytic compositions for esterification, transesterification and polycondensation reactions, a process for the catalysis of said reactions employing such catalytic compositions and polyesters or resins obtainable by this process.

The present invention relates to catalytic compositions for esterification, transesterification and polycondensation reactions, a process for the catalysis of said reactions employing such catalytic compositions and polyesters or resins obtainable by this process.

Catalytic systems containing organotin compounds are widely known. JP-A 06-248060, JP-A 03-284414 and JP-A 03-218511 describe catalyst systems based on organo tin compounds and trivalent and pentavalent heteroatom compounds especially phosphorous ligands, used in the ring opening polymerization of lactides. These systems are used to optimize the mechanical and thermal resistance of the polymer.

The application of such catalytic compositions for carrying out or accelerating other reactions has not been reported so far.

In contrast, DE-A-101 21 542 reports further that e.g. stabilizers containing heteroatoms are used for quenching the catalyst within the esterification, transesterification or pre-condensation step as these compounds form inactive products together with the catalyst.

Furthermore, special processes are known in which defined catalyst and stabilizer concentrations and defined locations for their addition are used. Herein the stabilizer is added after the catalyst. According to DE-A-19 50 997 it is common to deactivate the transesterification catalyst with a suited amount of a trivalent or pentavalent heteroatom containing compound by coordination or covalent bonding. This is done to avoid a detrimental influence of the transesterification catalyst within the polycondensation reaction. The polycondensation catalyst is added after this deactivation, a further polycondensation stabilizer might be added later.

Furthermore is known that during the production of polyesters for some applications for example wrappings and technical yarns, a crystallization and polycondensation in the solid state is carried out (U.S. Pat. No. 4,064,112, U.S. Pat. No. 4,263,425, U.S. Pat. No. 5,362,844). In other applications, fibers or filaments are spun directly and direct preforms are produced in a process wherein an intermediate transfer into the solid state and a repeated remelting is not applied.

Conventional polyester compositions are connected with a series of disadvantages (general summary in: Handbook of polyester thermoplastics, 1st edition, Wiley-VCH, Weinheim, 2002). Among these disadvantages are in particular:

-   -   Necessity of high temperatures for the synthesis     -   High catalyst concentration (100-500 ppm [as metal])     -   Degradation processes under processing and polycondensation         conditions; for example formation of vinyl esters and due to the         formation of acetic aldehyde in polyethylene terephthalate         (PET), formation of acrolein in polypropylene terephthalate         (PPT) and tetrahydrofuran formation in polybutylene         terephthalate (PBT).     -   Limited use of the catalyst systems, dependent on the technology         of the process and the chemical structure of the substrate;         classic titanium based catalysts cannot be added for example         during the esterification- and/or pre/condensation step, as         these are readily hydrolyzed to inactivate titanium oxides.     -   Application of the catalyst system only in selected process         stages for example only during the esterifications- or only         during the transesterification- or only during the         polycondensation stage.     -   Optical turbidity of the produced polyester for example by         deposits of elementary metal impurities as this can occur by the         use of antimony based catalyst systems.     -   Discoloration of the polyester by the catalyst itself, for         example titanium based catalyst systems cause a yellow coloring         of the polymer or formation of chromophor by-products,         respectively.     -   Problematic metering and addition of catalysts and catalyst         formulations.

Object of the present invention is to provide a catalytic composition, suitable for catalyzing esterification, transesterification and polycondensation reactions, an improved process of esterification, transesterification and polycondensation reactions and the production of improved polyesters for bottles, films, foils, yarn, molded padding, resins for powder coatings and technical synthetic materials, which avoid the disadvantages of the prior art.

The problem is solved according to the invention by a catalytic composition according to claim 1, a process according to claim 6 and polyesters or resins according to claims 18 and 19.

The catalytic composition for esterification, transesterification and polycondensation reactions according to the invention contains a mixture of at least one organotin compound (compound I) of the general formula (I):

-   -   wherein     -   R1 is selected from the group of linear, branched or cyclic         alkyl groups having 1 to 40 carbon atoms, aryl groups having 1         to 40 carbon atoms, or substituents selected from the group:         —X-R^(A), wherein R^(A) is —CN, —COOH, —COO-methyl, —COO-ethyl,         —COO-n-propyl, —COO-isopropyl, —COO-n-butyl, —COO-2-butyl,         —COO-iso-butyl, —COO-tert-butyl, COO-n-pentyl, —COO-isopentyl,         —COO-neo-pentyl, —COO-tert-pentyl, COO-hexyl, —COO-heptyl,         —COO-n-octyl, —COO-iso-octyl, —COO-2-ethyl-1-hexyl,         —COO-2,2,4-trimethylpentyl, —COO-nonyl, —COO-decyl,         —COO-dodecyl, —COO-n-dodecyl, —COO-cyclopentyl, —COO-cyclohexyl,         —COO-cycloheptyl, —COO-methylcyclohexyl, —COO-vinyl,         —COO-1-propenyl, —COO-2-propenyl, —COO-naphtyl, —COO-anthranyl,         —COO-phenanthryl, —COO-o-tolyl, —COO-p-tolyl, —COO-m-tolyl,         —COO-tolyl, —COO-ethylphenyl, —COO-mesityl, —COO-benzyl,         —COO-phenyl, —COOC₂H₄OH, —COOC₃H₆OH, —COOC₄H₈OH,         —COOCH₂C(CH₃)₂CH₂OH; and —X— is —CH₂—, —C₂H₄—, —C₃H₆—C₄H₈—,         —C₅H₁₀—, or —C₆H₁₂—;     -   R2 is selected from the groups of linear, branched or cyclic         alkyl groups having 1 to 40 carbon atoms, aryl groups having 1         to 40 carbon atoms and anionic ligands with O-coordination of         the group selected from −O, —OH, linear, branched or cyclic         alkyl or arylcarboxy groups having 1 to 40 carbon atoms, linear,         branched or cyclic alkyl-, and aryl alcoholate groups having 1         to 40 carbon atoms;     -   R3 and R4 independently each are selected from the groups of         anionic ligands with O-coordination of the group selected from         −O, —OH, linear, branched or cyclic alkyl groups or arylcarboxy         groups having 1 to 40 carbon atoms, linear, branched or cyclic         alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms         and anions of a mineral acid selected from the group of         sulphate, sulphite, phosphate, halogen- or pseudohalogen anion         and at least one compound (compound II) according to one of the         formulae (II), (III) and/or (IV),         X_(m)(R′)_(n)  (Formula II)         O═X_(m)(R′)_(o)  (Formula III)         (O═)_(r)X_(m)O_(p)(R′)_(q)  (Formula IV)         wherein X is a heteroatom selected from the group consisting of         N, P, Si, Cl, Br, I or S,     -   m is an integer from 1 to 5,     -   n is an integer from 1 to 5,     -   o is an integer from 1 to 5,     -   p is an integer from 0 to 5,     -   q is an integer from 0 to 5,     -   r is an integer from 0 to 3, wherein     -   R′ in formula (II) denotes n different or identical groups, each         being independent from each other selected from the group of         linear, branched or cyclic alkyl groups having 1 to 40 carbon         atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands         with O-coordination selected from the group of −O, —OH, linear,         branched or cyclic alkyl-, and aryl alcoholate groups having 1         to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion,     -   R′ in formula (III) denotes o different or identical groups,         each being independent from each other selected from the group         of linear, branched or cyclic alkyl groups having 1 to 40 carbon         atoms, aryl groups having 1 to 40, anionic ligands with         O-coordination selected from the group of −O, —OH, linear,         branched or cyclic alkyl-, and arylalcoholate groups having 1 to         40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion,         R′ in formula (IV) denotes q different or identical groups, each         being independent from each other selected from the group of         linear, branched or cyclic alkyl groups having 1 to 40 carbon         atoms, aryl groups having 1 to 40, anionic ligands with         O-coordination selected from the group of −O, —OH, linear,         branched or cyclic alkyl-, and arylalcoholate groups having 1 to         40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion.

Said catalytic compositions proved highly effective in the catalysis of esterification, transesterification, polycondensation, polyesterification and polytransesterification reactions.

It has to be pointed out that according to the invention compound I and compound II form a physical mixture and do not chemically react with each other. That means compound I and compound II are neither connected by a complex nor a covalent bond. For example, in the case that compound II is a phosphorous compound this is confirmed by the ³¹P NMR data of the physical mixture of compound I and compound II.

Preferred metal ions according to the invention include NH₄, Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Zn, B, Al, Sc, Y.

Preferred examples for compound I are defined by R1=methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, iso-pentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2-ethyl-1-hexyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, vinyl, 1-propenyl, 2-propenyl, naphthyl, anthranyl, phenanthryl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, or R1 a substituent from the group: —X-R^(A) with R^(A)=—CN, —COOH, —COO-methyl, —COO-ethyl, —COO-n-propyl, —COO-iso-propyl, —COO-n-butyl, —COO-2-butyl, —COO-iso-butyl, —COO-tert-butyl, —COO-n-pentyl, —COO-isopentyl, —COO-neo-pentyl, —COO-tert-pentyl, —COO-hexyl, —COO-heptyl, —COO-n-octyl, —COO-iso-Octyl, —COO-2-Ethyl-1-hexyl, —COO-2,2,4-trimethylpentyl, —COO-nonyl, —COO-decyl, —COO-dodecyl, —COO-n-dodecyl, —COO-cyclopentyl, —COO-cyclohexyl, —COO-cycloheptyl, —COO-methylcyclohexyl, —COO-Vinyl, —COO-1-propenyl, —COO-2-propenyl, —COO-naphtyl, —COO-ahthranyl, —COO-phenanthryl, —COO-o-tolyl, —COO-p-tolyl, —COO-m-tolyl, —COO-xylyl, —COO-ethylphenyl, —COO-mesityl, —COO-benzyl, —COO-phenyl, —COOC₂H₄OH, —COOC₃H₆OH, —COOC₄H₈OH, —COOCH₂C(CH₃)₂CH₂OH; with —X—: —CH₂—, —C₂H₄—, —C₃H₆—, —C₄H₈—, —C₅H₁₀—, —C₆H₁₂—.

Especially preferred substituents according to the invention are: methyl, n-butyl, n-octyl und n-dodecyl.

According to the invention —X— is preferably —C₂H₄—, and preferred moieties R^(A) are —CN, —COOH, —COO-methyl, —COO-ethyl.

Preferred examples for R2 are according to the invention:

-   a) methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl,     tert-butyl, n-pentyl, iso-pentyl, neo-pentyl, tert-pentyl, hexyl,     heptyl, n-octyl, iso-octyl, 2-ethyl-1-hexyl, 2,2,4-trimethylpentyl,     nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl,     cycloheptyl, methylcyclohexyl, vinyl, 1-propenyl, 2-propenyl,     naphthyl, anthranyl, phenanthryl, o-tolyl, p-tolyl, m-tolyl, xylyl,     ethylphenyl, mesityl, phenyl, benzyl. Favored substituents for the     invention are: Methyl, butyl, octyl and dodecyl, or -   b) 0, OH, methanolate, ethanolate, n-propanolate, iso-propanolate,     n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate,     n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate,     2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate,     iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate,     dodecanolate, n-dodecanolate, cyclopentanolate, cyclohexanolate,     cycloheptanolate, methylcyclohexanolate, glycolate, glycerate,     pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate,     2-ethyl-1-hexanolate, formiate, acetate, propionate, butyrate,     valeriate, caprate, caprylate, caprinate, laurate, laureate,     2-ethyl-1-hexanoate, neodecanoate, palmitate, stearate, benzoate,     terephthalate, phthalate, isoterephthalate, acrylate, methacrylate,     crotonate, isocrotonate, vinylacetate, oleate, sorbate, linolate,     linolenate, trifluoracetate, p-toluolsulfonate, oxalate, malonate,     succinate, glutarate, adipate, fumarate, maleinate, carboxylates of     the following monoesters: methylmaleicacid monoester,     ethylmaleicacid monoester butylmaleicacid monoester,     n-propylmaleicacid monoester, iso-propyl-maleicacid monoester,     n-butylmaleicacid monoester, 2-butylmaleicacid monoester,     iso-butylmaleicacid monoester, tert-butylmaleicacid monoester,     n-pentylmaleicacid monoester, isopentylmaleicacid monoester,     neo-pentylmaleicacid monoester, tert-pentylmaleicacid monoester,     2-methyl-1-butylmaleicacid monoester, hexylmaleicacid monoester,     heptylmaleicacid monoester, n-octylmaleicacid monoester,     iso-octylmaleicacid monoester, 2,2,4-trimethylpentylmaleicacid     monoester, nonylmaleicacid monoester, decylmaleicacid monoester,     dodecylmaleicacid monoester, n-dodecylmaleicacid monoester,     cyclopentylmaleicacid monoester, cyclohexylmaleicacid monoester,     cycloheptylmaleicacid monoester, methylcyclohexylmaleicacid     monoester, glycolmaleicacid monoester, glycerolmaleicacid monoester,     pinakolmaleicacid monoester, neopentylglycolmaleicacid monoester,     vinylmaleicacid monoester, propargylmaleicacid monoester and     2-ethyl-1-hexylmaleicacid monoester, citrate, lactate, tartrate,     naphtenate, naphthalen-2,6-dicarboxalate,     naphthalene-1,6-dicarboxalate, F, Cl, ClO, ClO₂, ClO₃, ClO₄, Br, J,     CN, SCN, OCN, sulphate, hydrogensulphate, sulphite,     hydrogensulphite, sulphide, phosphate, hydrogenphosphate,     dihydrogenphosphate, bis(2-ethyl-1-hexyl)phosphate, butylphosphate,     dibutylphosphate, 3-phosphonopropionate, phenylphosphonacid,     benzolphosphonigacid, p-aminophosphonacid, n-octylphosphonacid     favored substituents are: O, OH, laureate, 2-ethyl-1-hexanoate,     neodecanoate, oxalate, 2-ethyl-1-hexylmaleicacid monoester and     acetate.

Preferred examples for R3 and R4 are according to the invention: 0, OH, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclopentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate, formiate, acetate, propionate, butyrate, valeriate, caprate, caprylate, caprinate, laureate, 2-ethyl-1-hexanoate, neodecanoate, palmitate, stearate, benzoate, terephthalate, phthalate, isoterephthalate, acrylate, methacrylate, crotonate, isocrotonate, vinylacetate, oleate, sorbate, linolate, linolenate, trifluoracetate, p-toluolsulfonate, oxalate, malonate, succinate, glutarate, adipate, fumarate, maleinate, methylmaleicacid monoester, ethylmaleicacid monoester, butylmaleicacid monoester, n-propylmaleicacid monoester, iso-propylmaleicacid monoester, n-butylmaleicacid monoester, 2-butylmaleicacid monoester, iso-butylmaleicacid monoester, tert-butylmaleicacid monoester, n-pentylmaleicacid monoester, isopentylmaleicacid monoester, neo-pentylmaleicacid monoester, tert-pentylmaleicacid monoester, 2-methyl-1-butylmaleicacid monoester, hexylmaleicacid monoester, heptylmaleicacid monoester, n-octylmaleicacid monoester, iso-octylmaleicacid monoester, 2,2,4-trimethylpentylmaleicacid monoester, nonylmaleicacid monoester, decylmaleicacid monoester, dodecylmaleicacid monoester, n-dodecylmaleicacid monoester, cyclopentylmaleicacid monoester, cyclohexylmaleicacid monoester, cycloheptylmaleicacid monoester, methylcyclohexylmaleicacid monoester, glycolmaleicacid monoester, glycerolmaleic acid monoester, pinacolmaleicacid monoester, neopentylglycolmaleicacid monoester, vinylmaleicacid monoester, propargylmaleicacid monoester and 2-ethyl-1-hexylmaleicacid monoester, citrate, lactate, tartrate, naphtenate, naphthalene-2,6-dicarboxalate, naphthalene-1,6-dicarboxalate, F, Cl, ClO, ClO₂, ClO₃, ClO₄, Br, J, CN, SCN, OCN, sulphate, hydrogensulphate, sulphite, hydrogensulphite, sulphide, phosphate, hydrogenphosphate, dihydrogenphosphate, bis(2-ethyl-1-hexyl)phosphate, butylphosphate, dibutylphosphate, 3-phosphonopropionate, phenylphosphonacid, benzoenephosphonigacid, p-aminophosphonacid, n-octylphosphonacid. Most preferred substituents are: O, OH, Cl, laureate, 2-ethyl-1-hexanoate, neodecanoate, oxalate, 2-ethyl-1-hexylmaleicacid monoester and acetate.

Preferred examples for compound II of the invention are phosphites, phosphines, phosphonic acid esters, pyrophosphates, alkaline halogenides, earth alkaline halogenides, aluminum halogenides.

According to the invention combinations with the following examples of compound II are particularly preferred: Formula II (X═P): trioctyl-, triisooctyl-, trilauryl, tridecyl-, tridodecyl-, triisododecyl-, tritridecyl-, tripentadecyl-, trioleyl, tristearyl-, triphenyl-, trikresyl-, tris-nonylphenol, tris-2,4-t-butyl-phenyl- or tricyclohexylphosphite.

Further preferred phosphites of several aryl-dialkyl or alkyl-diarylphosphite may be advantageously applied, such as phenyldi-octyl-, phenyldidecyl-, phenyldidodecyl-, phenylditridecyl-, phenylditetradecyl-, phenyldipentadecyl-, octyldiphenyl-, decycidiphenyl-, undecyldiphenyl-, dodecyidiphenyl-, tridecyidiphenyl-, tetradecyldiphenyl-, pentadecyldi-phenyl-, oleyldiphenyl-, stearyldiphenyl-und dodecyl-bis-2,4-di-t-butylphenylphosphite, tris(2,4-di-tert-butylphenyl)phosphite, diphenyl-isodecylphosphite.

Also phosphites of several di- or polyols are very well suited and therefore preferred, e.g. phenylneopentylenglycolphosphite, heptakis-(dipropyleneglycol)triphosphite, 2,4,6-tri-tert-butylphenyl-2-butyl-2-ethyl-1,3-propandiolphosphite, bis(2,4-tri-tert-butylphenyl)penta-erythritoldiphosphite, tetraphenyldipropylenglykoldiphosphite, polydi-propyleneglykolphenylphosphite, tetramethylolcyclohexanol-decyidi-phosphite, tetramethylolcyclohexanol-butoxyethoxy-ethyldiphosphite, tetramethylolcyclohexanol-nonylphenyldiphosphite, bis-nonylphenyl-di-trimethylolpropanediphosphite, bis-2-butoxyethyl-di-trimethylol-propan-ediphosphite, trishydroxyethylisocyanurat-hexadecyltriphosphite, tris(dipropyleneglycol)phosphite, poly-4,4′-isopropylidendiphenol-c12-15-alcoholphosphite, diisodecylpentaerythritoldiphosphite, didecylpenta-erythritdiphosphite, distearylpentaerythritdiphosphite, also mixtures of these phosphites and aryl/alkylphosphite-mixtures of the statistic composition (H₁₉C₉-C₆H₄)O_(1,5)P(OC_(12,13)H_(25,27))_(1,5) or [C₈H₁₇—C₆H₄—O-]₂P[i-C₈H₁₇O] (H₁₉C₉-C₆H₄)O_(1,5)P(OC_(9,11)H_(19,23))_(1,5) are suitable as well as phosphines with R1′, R2′, R3′=methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl and also DIOP, Chiraphos and Norphos.

According to the invention especially favored are heteroatom compounds II including heteroatoms such as according to formula II wherein R1′, R2′ and R3′ are each independently selected from C₆H₅, OC₆H₅ and OC₄H₉.

Moreover, according to the invention mixtures of compound I with a compound II according to formula III are particularly preferred, such as e.g. (X═P): R1′, R2′, R3′=Methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, iso-pentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, vinyl, 1-propenyl, 2-propenyl naphthyl, anthryl, phenanthryl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, isopentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclopentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate, neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate, ethyleneglycol, diethyleneglycol, triethyleneglycol und benzylalcoholate and for X=2: tetramethylpyrophosphate, tetra ethylpyrophosphate, tetrakis-n-propylpyrophosphate, tetrakis-iso-propyl pyrophosphate, tetrakis-n-butylpyrophosphate, tetrakis-2-butylpyro-phosphate, tetrakis-iso-butylpyrophosphate, tetrakis-tert-butylpyro-phosphate, tetrakis-n-pentylpyrophosphate, tetrakis-iso-pentylpyro-phosphate, tetrakis-neo-pentylpyrophosphate, tetrakis-tert-pentylpyro-phosphate, tetrahexylpyrophosphate, tetraheptylpyrophosphate, tetrakis-n-octylpyrophosphate, tetrakis-iso-octylpyrophosphate, tetrakis-2-ethyl-1-hexylpyrophosphate, tetrakis-2,2,4-trimethylpentyl-pyrophosphate, tetranonylpyrophosphate, tetradecylpyrophosphate, tetradodecylpyrophosphate, tetrakis-n-dodecylpyrophosphate, tetra-cyclopentylpyrophosphate, tetracyclohexylpyrophosphate, tetracyclo-heptylpyrophosphate, tetrakis-methylcyclohexylpyrophosphate, tetra-naphthylpyrophosphate, tetraanthrylpyrophosphate, tetraphenanthryl-pyrophosphate, tetrakis-o-tolylpyrophosphate, tetrakis-p-tolylpyro-phosphate, tetrakis-m-tolylpyrophosphate, tetraxylylpyrophosphate, tetrakis-ethylphenylpyrophosphate, tetramesitylpyrophosphate, tetra-phenylpyrophosphate, tetrabenzylpyrophosphate or R1′, R2′=Methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, vinyl, 1-propenyl, 2-propenyl naphtyl, anthryl, phenanthryl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, isopentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclo-pentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate, ethylenglycol, dieethylene-glycol, triethylenglycol and benzylalcoholate, R3′=H such as e.g. diphenylphosphite. Triphenylphosphinoxide, triethylphosphate, tributyl-phosphate, triphenylphosphate, tris(triethylenglycol)phosphate and diphenylphosphite are especially preferred.

Further, according to the invention mixtures of compound I with one or more of the following examples of compound II are particularly preferred (Formula II, X═N): Trioctyl-, trilsooctyl-, trilauryl, tridecyl-, tridodecyl-, triisododecyl-, tritridecyl-, tripentadecyl-, trioleyl, tristearyl-, triphenyl-, trikresyl-, tris-nonylphenol, tris-2,4-t-butyl-phenyl-, tricyclohexylamine, also amines with a composition R1′, R2′, R3′=independent, the same or different: methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl are suitable, as well as R1′, R2′, R3′, R4′=H, R5′=Cl, or R1′, R2′, R3′, R4′ H, R5′=Br.

Mixtures of compound I with one or more of the following examples of compound II of formula II are according to the invention preferred (X═Si): R1′, R2′, R3′=independent, the same or different: methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, O-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, R4′=O, OH, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclo-pentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate; or R1′ and/or R2′=methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, R2′, R3′, R4′=independent, the same or different: 0, OH, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclo-pentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate; or R1′=methyl, ethyl, n-propyl, iso-propyl, n-butyl, 2-butyl, iso-butyl, tert-butyl, n-pentyl, isopentyl, neo-pentyl, tert-pentyl, hexyl, heptyl, n-octyl, iso-octyl, 2,2,4-trimethylpentyl, nonyl, decyl, dodecyl, n-dodecyl, cyclopentyl, cyclohexyl, cycloheptyl, methylcyclohexyl, o-tolyl, p-tolyl, m-tolyl, xylyl, ethylphenyl, mesityl, phenyl, benzyl, R2′, R3′, R4′=O, OH, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclopentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate; or R1′, R2′, R3′, R4′=independent, the same or different: O, OH, methanolate, ethanolate, n-propanolate, iso-propanolate, n-butanolate, 2-butanolate, iso-butanolate, tert-butanolate, n-pentanolate, iso-pentanolate, neo-pentanolate, tert-pentanolate, 2-methyl-1-butanolate, hexanolate, heptanolate, n-octanolate, iso-octanolate, 2,2,4-trimethylpentanolate, nonanolate, decanolate, dodecanolate, n-dodecanolate, cyclopentanolate, cyclohexanolate, cycloheptanolate, methylcyclohexanolate, glycolate, glycerate, pinacolate neopentylglycolate, vinylalcoholate, propargylalcoholate, 2-ethyl-1-hexanolate. Especially preferred according to the invention are mixtures with the following examples of compound II: Isobutylisopropyl dimethoxysilan, diisopropyl dimethoxysilan, diisbbutyldimethoxysilan, dicyclopentyl dimethoxysilan, n-propyltrimethoxysilan, isobutyl-sec.-butyl dimethoxysilan, cyclohexylisobutyl dimethoxysilan, cyclo-pentylisobutyl dimethoxysilan, di-sec.-butyl dimethoxysilan, dicyclohexyl dimethoxysilan, isobutylmethyl dimethoxysilan.

Mixtures of compound I with one or more of the following examples of compound II of formula II are according to the invention preferred (X═Cl or Br or I, with m=1): R1′=NH₄, Li, Na, K, Rb, for m=2: R1′=Cs, Mg, Ca, Sr, Ba, Zn for m=3: R1′=B, Al, Sc, Y, for m=4: R1′=Ti, Zr, Hf.

Also, mixtures of compound I with one or more of the following examples of compound II of formula III are according to the invention preferred, such as: NaClO₂, KClO₂, HClO₂, HClO₃, KClO₃, NaClO₃, HClO₄, NaClO₄, KClO₄, and, particularly preferred, NaCl, AIC13, KCl, NaBr, KBr, NaClO₄ and KClO₄ and their respective hydrates.

Moreover, mixtures of compound I with one or more of the following examples of compound II of formula III are according to the invention preferred (X═S): Na₂SO₄, K₂SO₄, MgSO₄, CaSO₄, SrSO₄, BaSO₄, Al₂(SO₄)₃, NaAl(SO₄)₂, NH₄Al(SO₄)₂, KAl(SO₄)₂ and their hydrates, particularly preferred are Al₂(SO₄)₃, NaAl(SO₄)₂, NH₄Al(SO₄)₂.

The molar ratio of compound I to compound II may by advantage be 1:0.001 to 1:200, preferred is a ratio of 1:0,01 to 1:20.

The composition of compound I and/or compound. II may contain suspension agents or solvents to improve reaction kinetics and yield.

The invention further provides a process for the continuous or batchwise catalysis of esterification, transesterification, polyesterification, polytransesterification reactions of an alcohol and an acid or acid derivative, e.g. an ester, anhydride or halogenide, characterized by employing a catalytic composition as defined above. This process may include the steps:

-   -   Preparation of a reaction mixture containing a polyvalent         alcohol and an acid or ester with at least two carboxy groups.     -   Addition of catalytic composition according to the invention.

At least two catalytic compounds I and II may be added to the reaction mixture in isolated form, as solid, dissolved in a suitable solvent, as a liquid or as suspension.

The employed carboxylic acid may be a monocarboxylic acid, di- or polycarboxylic acid. Among dicarboxylic acids, carboxylic acids containing at least two carboxyl groups, dicarboxylic acids such as e.g. terephthalic acid and/or 2,6-naphthalenedicarboxylic acid, isophthalic acid, 1,4-cyclohexane dicarboxylic acid, 1,6-naphthalene dicarboxylic acid, 4,4-bisphenyl dicarboxylic acids, adipic acid, phthalic acid, alkane dicarboxylic acids, halogen derivates of the mentioned dicarboxylic acids for example tetrabromo phthalic acid, and copolymers of the mentioned dicarboxylic acids or the esters of the mentioned carboxylic acids for example dimethyl terephthalate, bis(hydroxyethyl) terephthalate, 2,6-dimethyl naphthalate, 1,6-dimethyl naphthalate are particularly preferred.

The alcohols employed in the process according to the invention may be mono-, di- or polyvalent.

As di- or pblyvalent alcohols, alcohols such as ethylene glycol, 1,3-propanediol, 1,4-butanediol and/or 1,4-cyclohexanedimethanol, di-, triethylene glycol, polyglycols with a molecular weight below 1000 or neopentyl glycol, are particularly preferred.

Further, recycled polyester material might be used as co/monomer within the process based on the invention.

The inventors have shown that compound II, bearing a heteroatom as such neither catalyzes the esterification, nor transesterification, nor the polycondensation reaction. Surprisingly, an unexpected synergism between the metal catalyst (compound I) and the heteroatom compound (compound II) was found. The catalytic activity of selected systems of compound I can be increased according to the invention by approx. 50%.

According to the invention, the polycondensation is catalyzed and accelerated by a new compound system. It has been shown that in comparison to conventional catalytic systems less amounts of catalyst and stabilizer lead to comparable results. Furthermore, even high-viscous polyesters can be manufactured in a direct process in by far shorter polycondensation times. The novel mixtures according to the invention are further hydrolysis resistant and may be added either during the esterification phase and/or the precondensation phase as an active composition.

The catalytic composition of the invention shows a lower toxicity in comparison with conventional catalytic systems.

The preferred metal concentration of the catalytically effective metal compound (compound I) is 0.1 to 500 ppm (as Sn), in particular 10-200 ppm (as Sn) in relation to the acid or ester to be reacted.

The preferred concentration of the heteroatom containing compound (compound II) is 0.0001 ppm (as compound) to 1%, in particular 10-200 ppm in relation to the acid or ester to be reacted.

Particularly preferred is a process for a polyesterification reaction as defined above, characterized by reacting a dicarboxylic acid or a dicarboxylic acid derivative with a divalent alcohol.

Particularly preferred derivatives of mono-, di-, or polycarboxylic acids are esters or halogenides.

In the process of the invention hydroxycarboxylic acids such as p-hydroxybenzoic acid, salicylic acid, lactic acid, glycol acid or preferredly, derivatives thereof such as esters or ethers, and their co-polyesters with dicarboxylic acids and/or diols as described above may be reacted to the respective polyesters.

As a further compound a polyfunctional alcohol can be added to the reaction mixture. The polyfunctional alcohol, such as pentaerythritol can be added favored in a concentration of 0-500 ppm, in particular 50 ppm. The alcohol can be added together with compound I or separately, simultaneously, before or after, latest during the precondensation of the polyester. No influence on the effect of the other compounds occurs in this case.

The compounds I and/or II used for the production of polyester can be added during the period before the beginning of the esterification and/or transesterification until shortly before the end of the polycondensation, favored during the esterification and/or transesterification or before the precondensation.

A solvent or suspending agent may be added to compound I and/or compound II.

As solvents or suspending agents for the compounds I and/or II a mono-, di- or polyvalent alcohol such as e.g. an alkanediol may be employed. Preferred are 1,2-ethanediol, 1,3-propanediol, 1,4-butanediol, 2,2-dimethylpropan-1,3-diol.

The same solvent and/or suspending agent may be employed during manufacturing of the catalytic composition and said esterification, transesterification, polyesterification or polytransesterification reaction.

Alternative to this, also a different solvent and/or suspending agent may be employed during manufacturing of the catalytic composition and said esterification, transesterification, polyesterification or polytransesterification reaction.

Moreover, a solvent or suspending agent may be employed in the manufacturing step of the catalytic composition being selected from the group of mono-, di- or polyvalent alcohols that is reacted in said esterification, transesterification, polyesterification or polytransesterification reaction.

Further an organic liquid may be employed as solvent or suspending agent for the catalytic composition that is indifferent with respect to the polyester production process. Indifferent organic liquids are e.g. alkanes, cycloalkanes or benzene derivatives (for example benzene, toluene, xylenes). Also water or a mixture of water with an alcohol or a polyvalent alcohol is suited as solvent and/or suspending agent according to the invention.

Further additives for a color correction such as cobalt salts or organic dyes or pigments might be added to the reaction mixture, usually in amounts of 0.00001-5% by weight with respect to the acid or ester to be reacted.

Subject of the invention are further polycondensation products, produced by the described process of esterification, transesterification, polyesterification, polytransesterification with the use of the catalytic compositions according to the invention.

Furthermore, subject of the invention are polyester for bottles, films, foils, yarn, molded padding, resins for powder coatings and technical synthetic materials, obtainable by the process according to the invention.

The polyester available by the process according to the invention shows comparable qualities for the processability in comparison with conventional polyesters for example catalyzed by antimony. In comparison with usual high-viscous melt polymerisations, resins produced with the compounds described in the invention show a relatively low content of acetic aldehyde. In particular the polyesters synthesized with the process according to the invention show a narrow molecular weight distribution, a high translucency and give a polymer with a high, desired blue shift. A polymer of high viscosity is, unlike the state of the art using Sb catalysts, obtained without difficulty.

In the case of the inventive use of compound I with R1=—X-R^(A) the organotin catalyst is incorporated into the polymer by the means of an ester bond, that means the organotin species can only be released out of the polymer resin by its total destruction.

The polymers, produced with catalysts based on the invention show a high blue shift (negative b-values; color values are determined by using the CIE-Lab 100 color system with spectral reference beam color measuring instrument LUCI 100, Dr. Lange).

Polyesters, produced according to the invention employing a catalytic composition according to the invention show less by-products such as acetic aldehyde in polyethylene terephthalate (PET) in comparison with conventional techniques.

The polyesters produced according to the process described in the invention are made by esterification or transesterification with the use of the composition of compound I and/or compound II described in the invention and optionally subsequent polycondensation.

Preferred polyesters according to the invention are a) polyethylene terephthalate (PET), containing 0.1-10 mass % di-ethylene glycol and 0-10 mass % of isophthalic acid, 2-hydroxyisophthalic acid, p-hydroxyisophthalic acid, 2,6-naphthalene dicarboxylic acid and/or 1,4-cyclohexane dimethanole as co-monomer; b) polyester for powder coatings mainly poly-2,2-dimethylpropyl-1,3-terephthalate; c) polypropylene terephthalate (PPT); d) polyester polyols as for example polydiethyleneglycol terephthalate; e) polybutylene terephthalate (PBT); f) polynaphthalene terephthalates (PNT), g) polyethylene naphthalate (PEN).

The following examples further illustrate the invention without, however, limiting the invention. Unless otherwise indicated, parts and percentages relate to the weight, as in the remainder of the description.

EXAMPLES Example 1 Preparation of Catalytic Active Mixtures of compound I and compound II

Apparatus:

100 ml round bottom flask, magnetic stirrer, rotary evaporator.

Starting Materials, Quantities: butyltin tris[neodecanoate] 68.44 g [0.10 mol] a)triphenylphosphine 26.23 g [0.10 mol] b)triphenylphosphite 31.03 g [0.10 mol] c)triphenylphosphinoxide 27.83 g [0.10 mol] d)tributylphosphite 25.03 g [0.10 mol] Preparation:

The heteroatom compound II, dissolved in xylene (ethanol in the case of triphenylphosphine oxide) was given into the round bottom flask and stirred for 15 min. Butyltin tris[neodecanoat] dissolved in 50 ml xylene or ethanol, respectively was added to the mixture by the means of a tap funnel and stirred for an additional hour. The catalytic active system was obtained after removal of the solvent under reduced pressure.

Analysis:

-   ¹¹⁹Sn-NMR -   ³¹P-NMR -   catalyst system e)     Apparatus:

250 ml three necked round bottom flask, tap funnel, magnetic stirrer, water separator, rotary evaporator.

Starting Materials, Quantities: monobutyltin oxide 20.88 g [0.10 mol] neodecanoic acid  34.6 g [0.20 mol] triphenylphosphine 26.23 g [0.10 mol] Synthesis:

Monobutyltin oxide was dissolved in 150 ml xylene, triphenylphosphine, dissolved in 50 ml xylene and neodecanoic acid were added within 10 min. The mixture was heated under reflux until the water-formation stops. The product was obtained after filtration and removal of the solvent under reduced pressure.

Example 2 Catalyst Test by Synthesis of a Resin for Powder Coatings

Starting Materials, Quantities: terephthalic acid  83.07 g [0.50 mol] neopentylglycol 104.15 g [1.00 mol] (2,2-Dimethyl-1,3-propandiol) catalyst: 0.05%[m/m] calculated as Sn. Synthesis:

Catalyst, neopentyl glycol and terephthalic acid were given into a 250 ml three-necked round bottom flask. The mixture was heated to a maximum by the means of a heating jacket, the reaction water is distilled off and the amount formed is metered. The reaction time equals the time between the first water formation and the “clear point” of the reaction.

Example 3 Catalyst Test by Synthesis of a Resin for Powder Coatings with Physical Mixtures of Monobutyltin Oxide, Triphenylphosphine and Triphenylphosphite

Starting Materials, Quantities: terephthalicacid  83.07 g [0.50 mol] neopentylglycol 104.15 g [1.00 mol] (2,2-Dimethyl-1,3-propandiol) catalyst: f) 0.165 g monobutyltin oxide, 0.207 g triphenylphosphine g) 0.165 g monobutyltin oxide, 0.245 g triphenylphosphite Synthesis:

Catalyst, neopentyl glycol and terephthalic acid are given into a 250 ml three-necked round bottom flask. The mixture is heated to a maximum by the means of a heating jacket, the reaction water is distilled off and the amount is metered.

The reaction time equals the time between the first water formation and the “clear point” of the reaction.

Table 1 shows the acceleration of the reaction time in the described resin synthesis with the mixtures of (comparative) examples 1a, 1b, 1c, 1d, 1e and 1f, 1g in comparison with the uncatalized reaction or with monobutyltinoxide (0,05%[m/m]) as catalyst. TABLE 1 reaction time of the mixtures a-g. Sn- volume H₂O [ml]: catalyst content 15 30 45 60 75 90 [min] (0.05% tin) [%] min min min min min min 105 min 120 min 135 min 150 min 165 min 180 min time remarks without 1 1 2 3 4 300 aborted catalyst triphenylphosphine 0.05 3 4 4.5 300 aborted monobutyltin 0.05 9 14 23.5 155 clear, oxide colorless monobutyltin 0.05 2.5 4 5.5 7 9.5 11 13 15 17 18.5 21 22 180 hazy, trineodecanoate colorless a 0.05 3.5 6 9 11 14 16 100 clear, colorless b 0.05 2.5 7 9 12 15 17 100 clear, colorless c 0.05 2 6 9 13 15 18 97 clear, colorless d 0.05 4 8 12 16 19 85 clear, colorless e 0.05 5 8 12 16 18 60 clear, colorless f 0.05 8 14 16 100 clear, colorless g 0.05 4 6 8 10 14 14 16 16 120 clear, colorless

Example 4 Polycondensation of bis(2-hydroxyethyl) terephthalate (BHET)

Experimental Method:

-   Polycondensation equipment 1 (glass equipment) for the melt     polycondensation of BHET -   Tempering-bath (salt bath), polycondensation vessel (glass), screw     mixer (glass), vacuum pump, pressure gauge

As a polycondensation equipment, a round glass flask with round bottom was used, (internal diameter 2,6 cm, and 35 cm height, described in T. Johnson, Chem. Fibers International 46 (1996) 280; 49 (1999) 455). A horizontal vapor outlet was integrated into the upper third of the flask wall. A further extension tube near the bottom of the vessel allowed sampling from the polymer melt. The stirrer was a glassware screw mixer, reaching down to the ground (1,8 cm diameters). The mixer was operated with a rotation speed of 100 min⁻¹ and intermixed the melt with axially downward direction.

25,4 g (0,1 mol) BHET was filled into the polycondensation vessel, the catalyst (5 to 200 ppm as metal) was added and the vessel locked. Then the polycondensation vessel filled with the reaction mixture was evacuated three times and rinsed with dry nitrogen before it was immersed in the tempering-bath. The bath temperature was preset so that the desired internal temperature of 280° C. was reached in the polycondensation vessel. After the reaction mixture was melted, the stirrer was started and the vessel evacuated within 15 min onto a vacuum of 2×10⁻¹ mbar. The time of the first formation of glycol at the wall of the glass was regarded as t₀. The attainable final pressure for this equipment of approximately 4 to 5×10⁻² mbar, was reached after approx. 1 h experimental time, depending on the progress of the polycondensation. Through the sampling device samples could be taken by means of a VA steel wire, maintaining a nitrogen counterflow. At the end of the reaction up to 5 g could be taken from the vessel for further analysis. During the polycondensation, an average sampling required one minute, from breaking the vacuum to re-applying the vacuum. At the end of the polycondensation sampling was done within two minutes after aerating the vacuum.

PET Characterization

The determination of the intrinsic viscosities was performed as follows:

The relative solution viscosities η_(rel) for PET were determined in phenol (3 parts)/dichlorobenzene (2 parts) mixtures using 0.5 percent solutions at 25° C. The conversion of the relative solution viscosities into the intrinsic viscosity [η] was done according to BILLMEIER. $\eta_{intr} = {\frac{1}{4}\frac{\eta_{rel} - 1}{c + {3/4}} \times \frac{\ln_{\eta_{rel}}}{c}}$

From the intrinsic viscosities (IV) the average molecular weights Mn (number average) as well as the degrees of polymerization P_(n) were calculated. For PET applies: Mn=(1000×IV)^(1,5186); Pn=Mn/192.

The absolute viscosities were measured using the viscosimeter AVS 250 and the tempering-unit CT 1450 of Schott Geräte GmbH. Comparison measurements between different laboratories gave matching results.

The color values were determined using the CIE-LAB-Farbsystem (color system) by the spectral reference beam color measuring instrument LUCI 100, Dr. Lange.

The device STA 625 of Polymer Laboratories was used for TG and DSC-measurements.

The COOH end groups were determined by potentiometric titration of a cresol solution of the polymers with diluted aqueous NaOH.

BHET and the catalyst were introduced into the reaction vessel and rinsed well with nitrogen.

The reaction vessel was placed into the salt bath. Recording of reaction time started now. Within 15 min the pressure was lowered from 100 mbar to 0,09 mbar. At the end of the reaction a pressure of 0,04 mbar was reached.

The following table 2 shows the results of the polycondensation experiments for the catalyst e in comparison to Sb- and Ti-based catalysts (table 3). Criteria of the catalyst activity are the attainable molar mass in specific time periods, the increasing influence of the thermal degradation, recognizable by the flattening of the P_(n)-t-function as well as the color values of the polyester. The amount of the evolved ethanal (acetaldehyde) that directly correlates with the degree of thermal ester group cleavage is a further essential criterion of the catalyst suitability. The color values in the tables show the discoloration of the product, the a-values representing green/red-gradients and the b-values representing blue/yellow-gradients. Negative a-values correspond to green, negative b-values correspond to blue gradients. Blue shift is favored technologically. TABLE 2 Polycondensation of BHET with catalyst e. color values using the time Sn COOH M_(n) CIE-LAB-system [min] [ppm] η_(l) [μeq/g] [g/Mol] P_(n) L a b 30 123 0.2764 16 5104 26 34.19 −0.15 −0.14 60 123 0.5216 14 13386 69 33.84 −0.28 0.46 90 123 0.7152 19 21616 112 37.73 −0.44 1.05 120 123 0.8399 24 27588 143 36.54 −0.63 1.78

TABLE 3 Polycondensation of BHET with Sb and Ti catalysts. temperature time catalyst conc. Catalyst [° C.] [min] [ppm] P_(n) antimony 270 30 190 25 triacetate antimony 270 60 190 45 triacetate antimony 270 90 190 65 triacetate antimony 270 120 190 85 triacetate antimony 270 150 190 100 triacetate antimony 270 180 190 115 triacetate antimony 280 30 190 30 triacetate antimony 280 60 190 55 triacetate antimony 280 90 190 75 triacetate antimony 280 120 190 95 triacetate antimony 280 150 190 115 triacetate antimony 280 180 190 135 triacetate tetrabutyl titanate 280 30 20 45 tetrabutyl titanate 280 60 20 65 tetrabutyl titanate 280 90 20 85 tetrabutyl titanate 280 120 20 105 tetrabutyl titanate 280 150 20 125 tetrabutyl titanate 280 180 20 150

The comparative investigations for the catalytic activity of the selected tin compounds show that no noteworthy thermal decomposition is to be expected within 2 h of polycondensation time at temperatures of 280° C. Therefore it is absolutely possibly to synthesize even higher molecular weight polyethylene terephthalates by prolongation of the polycondensation time.

All examined tin compounds proved as high-activity catalysts for the polycondensation of BHET, which show significantly higher activity than stibious compounds. Their polytransesterification activity is superior to titanium alkoxides and titanium chelates. If required, they can be employed also in higher concentrations. 

1-19. (canceled)
 20. A catalytic composition useful for esterification, transesterification and polycondensation reactions, said catalytic composition comprising a mixture of: (A) at least one organotin compound of the general formula (I):

wherein R1 is selected from the group consisting of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, or substituents selected from the group: —X—R^(A), wherein R^(A) is —CN, —COOH, —COO-methyl, —COO-ethyl, —COO-n-propyl, —COO-isopropyl, —COO-n-butyl, —COO-2-butyl, —COO-iso-butyl, —COO-tert-butyl, —COO-n-pentyl, —COO-isopentyl, —COO-neo-pentyl, —COO-tert-pentyl, —COO-hexyl, —COO-heptyl, —COO-n-octyl, —COO-iso-octyl, —COO-2-ethyl-1-hexyl, —COO-2,2,4-trimethylpentyl, —COO-nonyl, —COO-decyl, —COO-dodecyl, —COO-n-dodecyl, —COO-cyclopentyl, —COO-cyclohexyl, —COO-cycloheptyl, —COO-methylcyclohexyl, —COO-vinyl, —COO-1-propenyl, —COO-2-propenyl, —COO-naphtyl, —COO-anthranyl, —COO-phenanthryl, —COO-o-tolyl, —COO-p-tolyl, —COO-m-tolyl, —COO-tolyl, —COO-ethylphenyl, —COO-mesityl, —COO-benzyl, —COO-phenyl, —COOC₂H₄OH, —COOC₃H₆OH, —COOC₄H₈OH, —COOCH₂C(CH₃)₂CH₂OH; and —X— is —CH₂—, —C₂H₄—, —C₃H₆—, —C₄H₈—, —C₅H₁₀—, or —C₆H₁₂—; R2 is selected from the group consisting of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms and anionic ligands with O-coordination of the group selected from —O, —OH, linear, branched or cyclic alkyl or arylcarboxy groups having 1 to 40 carbon atoms, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms; and R3 and R4 are each independently selected from the group consisting of anionic ligands with O-coordination of the group selected from —O, —OH, linear, branched or cyclic alkyl groups or arylcarboxy groups having 1 to 40 carbon atoms, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms and anions of a mineral acid selected from the group of sulphate, sulphite, phosphate, halogen- or pseudohalogen anion; and (B) at least one compound according to one of the formulae (II), (III) and/or (IV), X_(m)(R′)_(n)  (formula II) O═X_(m)(R′)_(o)  (formula III) (O═)_(r)X_(m)O_(p)(R′)_(q)  (formula IV) wherein X is a heteroatom selected from the group consisting of N, Si, Cl, Br, I or S, m is an integer from 1 to 5, n is an integer from 1 to 5, o is an integer from 1 to 5, p is an integer from 0 to 5, q is an integer from 0 to 5, r is an integer from 0 to 3, R′ in formula (II) denotes n different or identical groups, each being independent from each other and selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, —OH, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion, R′ in formula (III) denotes o different or identical groups, each being independent from each other and selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, —OH, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion, R′ in formula (IV) denotes q different or identical groups, each being independent from each other and selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, —OH, linear, branched or cyclic alkyl-, and arylalcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion, or X is P, then m is an integer from 1 to 5, n is an integer from 1 to 5, o is an integer from 1 to 5, p is an integer from 0 to 5 q is an integer from 0 to 5, r is an integer from 0 to 3, R′ in formula (II) denotes n different or identical groups, each being independent from each other and selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, —OH, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion, R′ in formula (III) denotes o different or identical groups, each being independent from each other and selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, —OH, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion, and R′ in formula (IV) denotes q different or identical groups, each being independent from each other selected from the group of linear, branched or cyclic alkyl groups having 1 to 40 carbon atoms, aryl groups having 1 to 40 carbon atoms, anionic ligands with O-coordination selected from the group of —O, linear, branched or cyclic alkyl-, and aryl alcoholate groups having 1 to 40 carbon atoms, H, Cl, Br, NH₄ ⁺ or a metal ion.
 21. The catalytic composition according to claim 20, wherein the metal ion is selected from the group consisting of NH₄, Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Zn, B, Al, Sc and Y.
 22. The catalytic composition according to claim 20, wherein (B) is a phosphite, a phosphine, a phosphonic acid ester, a pyrophosphate, an alkaline halogenide, an earth alkaline halogenide or aluminum halogenide.
 23. The catalytic composition according to claim 20, comprising a molar ratio of (A) to (B) of 1:0.001 to 1:200, in particular 1:0.01 to 1:20, respectively.
 24. The catalytic composition according to claim 20, further comprises a suspension agent or solvent.
 25. A process for the continuous or batchwise catalysis of esterification, transesterification, polyesterification, polytransesterification reactions of an alcohol and an acid or acid derivative, such as an ester, anhydride or halogenide, said process employing the catalytic composition as defined in claim
 20. 26. The process according to claim 25, employing an amount of (A) in the range of 0.1 to 1% by weight, in particular 10 to 200 ppm, with respect to the acid or ester to be reacted.
 27. The process according to claim 26, employing a concentration of (B) in the range of 0.0001 ppm to 1% by weight, in particular 10 to 200 ppm, with respect to the acid or ester to be reacted.
 28. The process according to claim 25, employing a concentration of (B) in the range of 0.0001 ppm to 1% by weight, in particular 10 to 200 ppm, with respect to the acid or ester to be reacted.
 29. The process according to claim 25, comprising reacting a dicarboxylic acid or a dicarboxylic acid derivative with a divalent alcohol in the polyesterification reaction.
 30. The process according to claim 25, employing derivatives of mono-, di or polycarboxylic acids selected from esters or halogenides.
 31. The process according to claim 25, comprising reacting hydroxycarboxylic acids or derivatives of hydroxycarboxylic acids in the esterification, transesterification, polyesterification or polytransesterification reaction.
 32. The process according to claim 31, employing derivatives of hydroxycarboxylic acids selected from esters or ethers.
 33. The process according to claim 25, employing a solvent or suspending agent added to (A) and (B).
 34. The process according to claim 33, employing an alkane mono-, di- or polyvalent alcohol as the solvent or suspending agent.
 35. The process according to claims 33, employing the same solvent and/or suspending agent during manufacturing of the catalytic composition and said esterification, transesterification, polyesterification or polytransesterification reaction.
 36. The process according to claim 35, employing a solvent selected from the group consisting of mono-, di- or polyvalent alcohols reacted in said esterification, transesterification, polyesterificatin or polytransesterification reaction.
 37. The process according to claim 33, employing a different solvent and/or suspending agent during manufacturing the catalytic composition and said esterification, transesterification, polyesterification or polytransesterification reaction.
 38. A composition comprising polyester for bottles, films, foils, yarn and/or molded padding, or resin for powder coatings or technical synthetic materials, obtained by the process according to claim
 25. 39. The polyester or resin composition according to claim 38, wherein said polyester is selected from the group consisting of polyethylene terephthalate, poly-2,2-dimethylpropyl-1,3-terephthalate, polypropylene terephthalate, polydiethyleneglycol terephthalate, polybutylene terephthalate, polynaphthalene terephthalate, polyethylene naphthalate, and mixtures thereof. 